YCr0.5Mn0.5O3 negative temperature coefficient perovskite ceramics sintered under reducing atmosphere: Microstructure and electrical properties - HAL Accéder directement au contenu
Article dans une revue Materials Science and Engineering: B Année : 2024

YCr0.5Mn0.5O3 negative temperature coefficient perovskite ceramics sintered under reducing atmosphere: Microstructure and electrical properties

Résumé

Instead of the common oxidizing atmosphere, three-phase high-temperature negative temperature coefficient (NTC) materials were prepared under reducing atmosphere from raw powders by conventional solid-state method in the Y2O3-Mn2O3-Cr2O3 ternary diagram. Owing to dilatometric analysis, the sintering stage was performed at 1500 ◦C for 1 h, 12 h, and 30 h under reducing atmosphere (1 % H2 – 99 % N2) whereas sintering is not reached at 1600 ◦C in air atmosphere. The sintered ceramics had 96 to 98 % of relative density. XRD patterns and SEM observations revealed that the sintered pellets consist of three phases: a phase with a structure similar to that of the orthorhombic perovskite YCrO3 and two other phases with structures close to that of Y2O3 and a solid solution of MnO. The results of electrical measurements as a function of temperature have shown that despite this dissociation of the phases, samples kept an NTC behavior with interesting characteristics for low and high temperatures: the resistivity increased slightly with dwell time, but the order of magnitude remained unchanged (105 Ω*cm) at 25 ◦C… Depending of the dwell time, activation energy obtained from material constant B varied from 0.276 eV at low temperature to 0.690 eV at high temperature. Such materials could be successfully used as potential candidates for temperature sensors applications in a wide range temperature from ambient temperature to 1000 ◦C.
Fichier principal
Vignette du fichier
Manuscrit with figures and tables-revised2.doc.pdf ( 1.1 Mo ) Télécharger
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-04636664, version 1 (05-07-2024)

Identifiants

Citer

A. Ngueteu Kamlo, J.M. Reboul, A.M. Cheumani Yona, M. Mouyane, J. Bernard, et al.. YCr0.5Mn0.5O3 negative temperature coefficient perovskite ceramics sintered under reducing atmosphere: Microstructure and electrical properties. Materials Science and Engineering: B, 2024, 299, pp.117037. ⟨10.1016/j.mseb.2023.117037⟩. ⟨hal-04636664⟩
0 Consultations
0 Téléchargements
comment ces indicateurs sont-ils produits

Altmetric

Partager

Gmail Facebook Twitter LinkedIn Plus